Portland Cement carries clinker, gypsum as setting regulator and it’s been grinded together with minor additional component. Complies with TS EN 197-1: 2012 standard.
It has early strength and ultimate strength due to it is high clinker content.
Portland Cement carries clinker, gypsum as setting regulator and it is grinded together with minor additional component. Complies with TS EN 197-1: 2012 standard, is a cement with a 28 days compressive strength of at least 52.5 MPa.
It has early strength and ultimate strength.
Portland Cement clinker, gypsum and up to 5% minor additive material are grinded together and produced in accordance with TS EN 197 -1 / March: 2002 “Cement - Part 1: General Cements - Composition, Properties and Conformity Criteria” standard. Cement with a compressive strength of at least 30 days and a minimum compressive strength of 28 days and a minimum of 52.5 MPa.
Portland Cement clinker, gypsum, 36-55% additive (Tras - Fly Ash) and up to 5% minor additional ingredient co-grinding TS EN 197 -1 / March: 2002 “Cement - Department It is a cement produced according to 1: General Cements Composition, Properties and Conformity Criteria ”, with a 2-day compressive strength of at least 10 and a 28-day compressive strength of at least 32.5 MPa and a maximum of 52.5 MPa.
As it contains high additives, its hydration temperature is low, it is more resistant to alkali-aggregate reaction and chemical external effects.
Portland Cement with a maximum C3A content of 5% carries; clinker, gypsum as setting regulator and it’s been grinded together with minor additional component. Complies with TS EN 197-1: 2012 standard.
Due to it’s low C3A effect It has the property of sulphate resistant. It is highly preferred in applications such as sea water, sewage, etc. that are exposed to high sulphate.
Portland Slag Cement, Portland Cement clinker, gypsum, 6-20% additive (Blast Furnace Slag) and up to 5% minor additional ingredient co-grinding TS EN 197 -1 / March: 2002 “Cement - Department 1: General Cements - Composition, Specifications and suitability criteria ”is a cement with a compressive strength of at least 20 days and a compressive strength of at least 42.5 MPa and a maximum of 62.5 MPa for 28 days.
It can be used with the benefit of blast furnace slag additive in environments exposed to high sulphate such as sea water and sewage.
Blast Furnace Slag Cement, Portland Cement clinker, gypsum, 36-65% additive (Blast Furnace Slag) and up to 5% minor additional ingredient co-grinding TS EN 197 -1 / March: 2002 “Cement - It is a cement with 7 days compressive strength of minimum 16 and 28 days of compressive strength of minimum 32.5 MPa and maximum of 52.5 MPa.
It can be used with the benefit of blast furnace slag additive in environments exposed to high sulphate such as sea water, sewage.
As it contains high additives, its hydration temperature is low and it is more resistant to alkali-aggregate reaction and chemical external effects.